Evaluation of multiple and single emission peak light emitting diode light curing units effect on the degree of conversion and microhardness of resin-based pit and fissure sealant

Abstract

Objective: The objective was to assess a multiple emission peak light-emitting-diode (LED) light-curing unit (LCU) by measuring the polymerization efficiency through the degree of conversion (DC) and Knoop microhardness (KHN) of a resin-based pit and fissure sealant at various light curing times and two distances compared to a single emission peak LED LCU. Method: Sixty disks of resin-based pit and fissure sealant (Delton, DENTSPLY, York, PA) samples (6x1mm) were fabricated (n=5/LCU/group). Prepared samples were polymerized using 10, 20 and 40 second curing time at 2 or 4 mm curing distances. The irradiance and radiant exposure received on the top/bottom surfaces of the samples were measured using the Managing Accurate Resin Curing-Resin Calibrator (MARC-RC) system. The samples were stored at 37°C for one hour. Then, the DC (n=3/surface) and KHN (n=5/surface) measurements were collected on the top and bottom surfaces using Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR) and a microhardness tester (Instron) utilizing 25-gm at 10 seconds dwell time, respectively. Multiple-way ANOVA was performed followed by Tukey test (α=0.05). Result: The irradiance from the multiple emission peak LED LCU was significantly higher than the single emission peak LED LCU (1312.6 and 768.3 mW/cm2) respectively. Moreover, the multiple emission peak LED LCU displayed significantly higher DC (82.5%) and microhardness (26.2 KHN) compared to the single emission peak LED LCU (75.5% DC and 21.2 KHN) when curing samples at 2 and 4 mm curing distances assessed using 10, 20 and 40-second curing times. The 10 second cure at 4 mm showed significantly lower DC and KHN values compared to the other groups. Conclusion: The multiple emission peak LED LCU demonstrated significantly higher irradiance, DC and KHN compared to the single emission peak LED LCU on a resin-based pit and fissure sealant at 2 and 4 mm curing distances and 10, 20 and 40 second curing times. Therefore, the multiple emission peak LED LCU performed higher than the single emission peak LED LCU.