  • Thumbnail Image
    Item
    Comparison of Internal Adaptation of Bulk-fill and Increment-fill Resin Composite Materials
    (2019-01) Alqudaihi, Fatema Sabri; Cook, N. Blaine; Diefenderfer, Kim E.; Bottino, Marco C.; Platt, Jeffrey A.; Cariology, Operative Dentistry and Dental Public Health, School of Dentistry
    Objectives: To evaluate 1) the internal adaptation of a light-activated incremental-fill and bulk-fill resin-based composite (RBC) materials by measuring the gap between the restorative material and the tooth structure and 2) the aging effect on internal adaptation. Methods and Materials: Seventy teeth with class I cavity preparations were randomly distributed into five groups; four groups were restored with bulk-fill RBCs: Tetric EvoCeram Bulk Fill (TEC), SonicFill (SF), QuiXX Posterior Restorative (QX), and X-tra fil (XF); the fifth group was restored with incremental-fill Filtek Supreme Ultra Universal Restorative (FSU). One-half of the specimens of each group were thermocycled. Each tooth was sectioned, digital images were recorded, and the dimensions of any existing gaps were measured. Data were analyzed using analysis of variance (α=0.05). Results: FSU had the smallest gap measurement values compared with the bulk-fill materials except QX and TEC (p≤0.008). FSU had the smallest sum of all gap category values compared with the bulk-fill materials, except QX (p≤0.021). The highest gap incidence and size values were found at the composite/adhesive interface. All aged groups had greater gap values in regard to the gap measurement and the sum of all gap categories compared with non-aged groups. Significance: The incrementally placed material FSU had the highest internal adaptation to the cavity surface, while the four bulk-fill materials showed varied results. Thermocycling influenced the existing gap area magnitudes. The findings suggest that the incremental-fill technique produces better internal adaptation than the bulk-fill technique.
  • Thumbnail Image
    Item
    The Influence of Distance on Radiant Exposure and Degree of Conversion Using Different Light-Emitting-Diode Curing Units
    (Allen Press, 2019-05) Al-Zain, A.O.; Eckert, G. J.; Platt, J. A.; Biomedical Sciences and Comprehensive Care, School of Dentistry
    Objectives: To investigate the influence of curing distance on the degree of conversion (DC) of a resin-based composite (RBC) when similar radiant exposure was achieved using six different light-curing units (LCUs) and to explore the correlation among irradiance, radiant exposure, and DC. Methods and Materials: A managing accurate resin curing-resin calibrator system was used to collect irradiance data for both top and bottom specimen surfaces with a curing distance of 2 mm and 8 mm while targeting a consistent top surface radiant exposure. Square nanohybrid-dual-photoinitiator RBC specimens (5 × 5 × 2 mm) were cured at each distance (n=6/LCU/distance). Irradiance and DC (micro-Raman spectroscopy) were determined for the top and bottom surfaces. The effect of distance and LCU on irradiance, radiant exposure, and DC as well as their linear associations were analyzed using analysis of variance and Pearson correlation coefficients, respectively (α=0.05). Results: While maintaining a similar radiant exposure, each LCU exhibited distinctive patterns in decreased irradiance and increased curing time. No significant differences in DC values (63.21%-70.28%) were observed between the 2- and 8-mm distances, except for a multiple-emission peak LCU. Significant differences in DC were detected among the LCUs. As expected, irradiance and radiant exposure were significantly lower on the bottom surfaces. However, a strong correlation between irradiance and radiant exposure did not necessarily result in a strong correlation with DC. Conclusions: The RBC exhibited DC values >63% when the top surface radiant exposure was maintained, although the same values were not reached for all lights. A moderate-strong correlation existed among irradiance, radiant exposure, and DC.