ScholarWorksIndianapolis
  • Communities & Collections
  • Browse ScholarWorks
  • English
  • Català
  • Čeština
  • Deutsch
  • Español
  • Français
  • Gàidhlig
  • Italiano
  • Latviešu
  • Magyar
  • Nederlands
  • Polski
  • Português
  • Português do Brasil
  • Suomi
  • Svenska
  • Türkçe
  • Tiếng Việt
  • Қазақ
  • বাংলা
  • हिंदी
  • Ελληνικά
  • Yкраї́нська
  • Log In
    or
    New user? Click here to register.Have you forgotten your password?
  1. Home
  2. Browse by Subject

Browsing by Subject "Adhesion to dentin"

Now showing 1 - 1 of 1
Results Per Page
Sort Options
  • Loading...
    Thumbnail Image
    Item
    Comprehensive Evaluation of Long-Term Dentin Bond Strength, Water Sorption, Solubility, and Degree of Conversion of Self-Adhesive Resin Composites
    (Quintessence, 2024-09-17) Yao, Ye; Wu, Di; Cifuentes-Jimenez, Carolina Cecilia; Sano, Hidehiko; Alvarez-Lloret, Pedro; Yamauti, Monica; Tomokiyo, Atsushi; Biomedical and Applied Sciences, School of Dentistry
    Purpose: To evaluate the long-term microtensile bond strength (µTBS) to dentin, water sorption (WSP) and solubility (WSL), and degree of conversion (DC) of self-adhesive resin composites (SACs). Materials and methods: The mid-coronal dentin of human molars was exposed, and teeth were randomly assigned to five groups according to the SACs (n = 10): 1. FIT SA F03 (FIT); 2. Experimental (EXP); 3. Fusio Liquid Dentin (FLD); 4. Vertise Flow (VER); 5. Constic (CON). The µTBS was evaluated after 24 hours (24 h) and 6 months (6 m) storage. A scanning electron microscope examined failure modes and resin-dentin interfaces. The WSP and WSL (n = 5) were evaluated following ISO 4049:2019 specifications, and DC (n = 3) was measured using Raman spectroscopy. The statistical analyses were performed accepting a significance level of p = 0.05. Results: FIT, EXP, and FLD produced significantly higher µTBS median values than VER and CON after 24 h and 6 m (p 0.05). After 6m, the µTBS median of FIT and EXP significantly decreased (p 0.05), while FLD, VER, and CON showed no significant difference (p > 0.05). FLD and CON exhibited lower WSP than FIT, EXP, and VER (p 0.05). FLD presented the lowest (p 0.05), and VER revealed the highest WSL (p 0.05). FIT and EXP showed the highest (p 0.05), and VER demonstrated the lowest DC (p 0.05). Conclusions: Following the present study's design, SACs' bonding performance and physical properties remained restricted. Therefore, the application should be considered cautiously, and further clinical trials are necessary to evaluate their long-term performance.