    3D-Image Analysis of the Impact of Toothpaste Abrasivity on the Progression of Simulated Non-Carious Cervical Lesions
    (Elsevier, 2018) Sabrah, Alaa H.; Turssi, Cecilia P.; Lippert, Frank; Eckert, George J.; Kelly, Adam B.; Hara, Anderson T.; Cariology, Operative Dentistry and Dental Public Health, School of Dentistry
    Objectives To investigate the effect of toothpaste abrasive level on the progression of non-carious cervical lesions (NCCLs) using 3D-image subtraction. Methods Upper first premolars were allocated into seven groups (n = 16) of toothpaste/abrasive slurries: A-Zeodent113/5%, B-Zeodent124/10%, C-Zeodent103/15%, D-Sensodyne Pronamel, E-Crest Cavity-Protection, F-Crest Pro-Health-Whitening, and G-Deionized water (DIW). Teeth were mounted on acrylic blocks, and their root surfaces covered with acrylic resin, except for 2-mm near the cemento-enamel junction that was exposed to toothbrushing. Specimens were brushed with the slurries for 5000-, 15,000-, 35,000- and 65,000-strokes. Impressions were taken at baseline and after each brushing time, and then scanned by a 3D optical profilometer. Dentine volume loss was calculated by image subtraction software and subjected to mixed-model ANOVA and multiple comparison tests (α = 0.05). Results No significant differences among slurries were observed at 5000 and 15,000. At 35,000, F showed higher loss than all other groups except C, which did not differ from the others. At 65,000, F (4.19 ± 3.29 mm3) showed the highest loss, followed by C (2.33 ± 1.47 mm3), which differed from all the other groups except B (1.85 ± 0.91 mm3). Groups B, A (1.35 ± 0.65 mm3), D (1.17 ± 0.48 mm3), E (1.40 ± 0.68 mm3) and G (1.12 ± 0.73 mm3) did not differ from each other. Groups F and C showed significant increase of volume loss starting at 35,000, while B, A, D and E only at 65,000; no increase loss was observed for G. Conclusions 3D-image subtraction was able to quantify and differentiate tooth loss, but only at advanced stages. The progression of NCCLs was more evident and faster for highly abrasive slurries. Clinical significance Upon root dentin exposure, brushing with lower abrasive dentifrices is advisable to reduce the risk for NCCLs development.
  • Thumbnail Image
    Item
    Effects of air-abrasion pressure on the resin bond strength to zirconia: a combined cyclic loading and thermocycling aging study
    (XMLink, 2017-08) Al-Shehri, Eman Z.; Al-Zain, Afnan O.; Sabrah, Alaa H.; Al-Angari, Sarah S.; Al Dehailan, Laila; Eckert, George J.; Özcan, Mutlu; Platt, Jeffrey A.; Bottino, Marco C.; Biomedical and Applied Sciences, School of Dentistry
    Objectives To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide (Al2O3) particles at different pressures. Materials and Methods Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abrasion pressures (1, 2, and 2.8 bar), and each group was further divided into 2 groups depending on aging parameters (n = 12). Panavia F 2.0 was placed on pre-conditioned zirconia surfaces, and SBS testing was performed either after 24 hours or 10,000 fatigue cycles (cyclic loading) and 5,000 thermocycles. Non-contact profilometry was used to measure surface roughness. Failure modes were evaluated under optical and scanning electron microscopy. The data were analyzed using 2-way analysis of variance and χ2 tests (α = 0.05). Results The 2.8 bar group showed significantly higher surface roughness compared to the 1 bar group (p < 0.05). The interaction between pressure and time/cycling was not significant on SBS, and pressure did not have a significant effect either. SBS was significantly higher (p = 0.006) for 24 hours storage compared to CLTC. The 2 bar-CLTC group presented significantly higher percentage of pre-test failure during fatigue compared to the other groups. Mixed-failure mode was more frequent than adhesive failure. Conclusions CLTC significantly decreased the SBS values regardless of the air-abrasion pressure used.