Wu, LinminZhang, YiZhang, Jing2016-08-022016-08-022016-04-08Linmin Wu, Yi Zhang, and Jing Zhang. 2016, April 8. Finite element study of Li diffusion and stress in LiNi0.33Mn0.33Co0.33O2 cathode using microstructures reconstructed by synchrotron X-ray tomography. Poster session presented at IUPUI Research Day 2016, Indianapolis, Indiana.https://hdl.handle.net/1805/10539poster abstractLiNi0.33Mn0.33Co0.33O2 is a good substitute for LiCoO2 because of its good thermal stability and high energy density. In this study, the diffusion and stress in LiNi0.33Mn0.33Co0.33O2 cathode with realistic three-dimensional (3D) microstructures have been studied systematically. Synchrotron Xray tomography was used to obtain the 3D reconstructions of porous LiNi0.33Mn0.33Co0.33O2 microstructures. Li concentration distributions under various C-rates were investigated. The obtained charge/discharge curves under various C-rates were compared with the results from Newman’s model. The stress generation in the cathode was computed coupled with the diffusion. The hydrostatic stress, shear stress and von Mises stress in the particles were analyzed. The results show that the von Mises stress in particle boundaries is higher than the stress inside the particle due to the Li concentration gradient during discharge, which is consistent with the literature. Additionally, the von Mises stress near the particle contact region is much higher than other areas.en-USLiNi0.33Mn0.33Co0.33O2LiCoO2thermal stabilityhigh energy densitythree-dimensional (3D) microstructuresSynchrotron Xray tomographyPoster