Zhang, HanyinCai, LinlinGolub, MichaelZhang, YiYang, XuehuiSchlarman, KateZhang, Jing2018-05-092018-05-092018-01Zhang, H., Cai, L., Golub, M., Zhang, Y., Yang, X., Schlarman, K., & Zhang, J. (2018). Tensile, Creep, and Fatigue Behaviors of 3D-Printed Acrylonitrile Butadiene Styrene. Journal of Materials Engineering and Performance, 27(1), 57–62. https://doi.org/10.1007/s11665-017-2961-7https://hdl.handle.net/1805/16102Acrylonitrile butadiene styrene (ABS) is a widely used thermoplastics in 3D printing. However, there is a lack of thorough investigation of the mechanical properties of 3D-printed ABS components, including orientation-dependent tensile strength and creep fatigue properties. In this work, a systematic characterization is conducted on the mechanical properties of 3D-printed ABS components. Specifically, the effect of printing orientation on the tensile and creep properties is investigated. The results show that, in tensile tests, the 0° printing orientation has the highest Young’s modulus of 1.81 GPa, and ultimate strength of 224 MPa. In the creep test, the 90° printing orientation has the lowest k value of 0.2 in the plastics creep model, suggesting 90° is the most creep resistant direction. In the fatigue test, the average cycle number under load of 30 N is 3796 cycles. The average cycle number decreases to 128 cycles when the load is 60 N. Using the Paris law, with an estimated crack size of 0.75 mm, and stress intensity factor is varied from 352 to 700enIUPUI Open Access Policy3D printingacrylonitrile butadiene styreneadditive manufacturingArticle